FXGH-880 Inorganic Zinc-Rich Anticorrosive Primer

[Search Related Products]

FXGH-880 Inorganic Zinc-Rich Anticorrosive Primer

FXGH-880 Inorganic Zinc-Rich Anticorrosive Primers (Acquired the certification of European Union CE)


Characteristics: Excellent cathodic protection, anticorrosive, impact resistance, machine abrasion and organic solvent resistance property, initial hardness¡¢perfect thick coating property while construction¡¢heat resistance which can resist 400¡æ high temperature.

Uses: Mainly as anticorrosive of steel surface in bridge¡¢shipping boats¡¢oil chemical infrastructures¡¢containers¡¢steel structures
etc., also as a ues of primer.

Technical target:
Mixing ratio: A group portion: B group portion=4:1 (by weight)
Standard film thickness: dry: 50¦Ìm/coat
Academic spreading rate: 0.17kg/ ©O /50¦Ìm
Solid contents: 72.4%
Humidity requirement: below 85%
Drying time & coating interval

Temperature £¨¡æ£©

-10

0

10

20

30

Dry to touch£¨hrs£©

20

12

8

6

5

Dry semi-hard£¨hrs£©

5

3

2

1.5

1

Min. interval£¨hrs£©

36

24

18

12

10

Substrate treatment: Remove rust¡¢oxide skin and shop primer by abrasive blasting, reached ISO Sa2.5 grade

Matching:
Applicable substrate: cc
Applicable upper coatings: Epoxy Mica Iron Intermediate Paint, Modified Epoxy Nonferrous Metal Primers

Application Examples:

FXGH-880 Inorganic Zinc-Rich Anticorrosive Primer

FXGH-880 Inorganic Zinc-Rich Anticorrosive Primer